Home > Products > Colmonoy Nickel base powder > Colmonoy 7631-60F

Colmonoy 7631-60F

Colmonoy 7631-60F Nickel Base Powder Ni 7631-60F Powder Plants Heat Treating Equipment Prosthetic Devices

008615801826494

singoo@wl-allotech.com

8615801826494

Colmonoy 7631-60F

description1

Zipper closure 1/4 zip athletic pullovers for men. Stretchy, lightweight, fast-drying fabric for superior performance. REGULAR FIT - US standard sizes. An athletic fit that sits close to the body for a wide range of motion, designed for optimal performance and all day comfort. FEATURES - Quarter zip closure;Thumbholes on long sleeves to keep them in place during workout

Product Description

WL Allotech Alloy 7631-60F powder offers superior wear protection, it offers outstanding metallurgical and physical properties making them ideally suited to solving wear mechanisms such as abrasion, erosion, corrosion and high-temperatures encountered in service.

CLASSIFICATION: AWS A5.14
Common Name: Colmonoy 7631-60F

Chemical Composition(%)

B	C	Cr	Fe	Si	W	Ni
1.16	2.58	6.08	1.80	1.82	57.66	Bal.

Surface Preparation

Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the
surface to be coated. Note: It is best not to handle surfaces after cleaning.
Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide,
rough grind, or rough machine in a lathe.

Packing Details

Each bottle 5kg/bottles, 4 bottles pack in one carton,

then put cartons onto pallet or Box. OEM packing & label or customized packing methods available.

Applications

Aircraft gas turbines

steam turbine power plants

turbochargers and valves in reciprocating engines

prosthetic devices

heat treating equipment

pollution control equipment

coal gasification and liquefaction systems

components in pulp and paper mills.

Type we could offer

Trademark	Nominal Composition(%)									HRC	Application
Trademark	B	C	Cr	Fe	Mo	Si	W	Ni	Others	HRC	Application
WLNi-63	3.0	0.6	15.0	4.0		4.5		Bal.		58-61	Excellent abrasion and corrosion resistance.
WLNi-62	3.2	0.7	15.5	4.0		4.2		Bal.		56-64	shafts, sleeves, pump plungers, sucker rod couplings, bed knives, camshafts, bushings, mill guides, mixer blades, seal rings, brick manufacturing equipment, and conveyor screws.
WLNi-705	1.5	2.2	7.0	2.0		2.3	48.1	Bal.		56-63	protection from severe sliding abrasion. Used on screw conveyors and augers
WLNi-750	1.6	3.0	6.8	2.0		1.5	48.0	Bal.	Co: 6.0	57-63	A tough nickel-chromium-tungsten matrix alloy is used to hold extremely hard tungsten-carbide particles. Best used for the most severe abrasive conditions. Finished by grinding.
WLNi-225	0.8					2.3		Bal.	P:2.0	13-17	For glass container mould protection and restoration. Also used for rebuilding automotive parts (clutch components).
WLNi-226	0.8					2.2		Bal.	P:1.9	16-21	Blow heads, edges and repairs blow-blow plungers, guide rings, baffles
WLNi-227	1.1					2.8		Bal.	P:2.1	22-27	For glass container mould protection and restoration. Also used for rebuilding automotive parts (clutch components).
WLNi-234	1.0	0.15	4.0		3.0	2.8		Bal.	P:2.1	32-36	For glass container mould protection and restoration.
WLNi-4	2.1	0.4	10.0	2.8		2.4		Bal.		35-40	Aircraft gas turbines, steam turbine power plants, turbochargers and valves in reciprocating engines, prosthetic devices, heat treating equipment, pollution control equipment, coal gasification and liquefaction systems, and components in pulp and paper mills.
WLNi-7631-60F	1.16	2.58	6.08	1.80		1.82	57.66	Bal.			Aircraft gas turbines, steam turbine power plants, turbochargers and valves in reciprocating engines, prosthetic devices, heat treating equipment, pollution control equipment, coal gasification and liquefaction systems, and components in pulp and paper mills.
WLNi-42	2.0	0.4	10.0	2.5		3.0		Bal.		35-40	Less hardness and slightly less abrasion and corrosion resistance.
WLNi-22	1.0	0.1	0.05	0.03		3.0		Bal.		28-33	Bottle moulds, cast iron parts
WLNi-22-KW	1.0	0.1	0.05	0.03		3.0		Bal.	P:2.0	28-32	Aircraft gas turbines, steam turbine power plants, turbochargers and valves in reciprocating engines, prosthetic devices, heat treating equipment, pollution control equipment, coal gasification and liquefaction systems, and components in pulp and paper mills.